Flexible Magnetic Sheets
Magnetic rubber sheet is made by mixing with plastic or synthetic rubber using Newlife Technology! This is kind of high quality material and Barium Free! It has permanent magnetic property with excellent flexibility characteristics. It can be easily cut, slit, folded and twisted without damaging the magnetic power; the magnetic power is guaranteed not to reduce unnormal conditions.
Advantage of Magnetic Rubber Sheet
●Producible Range of thickness: 0.2~8mm (8~315mil)
●Custom thickness and width are available upon request
●advanced UV back coating protects from surface staining and sticking and it eliminates blocking
Popular Dimension of Magnetic Rubber Sheet
The size is customized, here below are some popular sizes for your reference.
|
Popular Sheet Size |
Length |
Thickness |
|
297x210mm |
0.4mm |
|
|
480x330mm |
0.5mm |
|
|
500x310mm |
0.76mm |
|
|
700x500mm |
0.8mm |
|
|
900x600mm |
1.2mm |
|
|
1000x620mm |
|
|
|
Roll Size are available, such as 30Mx620mm, 30Mx1200mm and ect. |
||
Material Types of rubber magnet sheet
|
Material |
Max. Energy Product |
|
a. Isotropic/semi Anisotropic Ferrite |
0.7-0.8MGOe |
|
b. Full Anisotropic Ferrite( High Energy Sheet) |
1.1-1.4MGOe |
|
c. Neodymium Flexible Material |
2.0-2.5MGOe |
Material Thickness of rubber magnet sheet
The popular thickness range of flexible magnet material is 0.4-1.5mm, but thicker material is available in high energy. The thicker the material the greater the pull. It is not in direct proportion, but the thicker the material the greater the pull increase. Eg:0.75mm thick material has a pull of 44 gram/cm2 and if proportional the 1.5mm thick material would be 88gram/cm2, but in fact it is actually far higher at 140 gram/cm2.
Typical Pull Characteristics:
|
Material Thickness(mm) |
Pull (Gram/cm2) |
|
0.4 |
19 |
|
0.5 |
28 |
|
0.75 |
44 |
|
1.5 |
140 |
Magnetic properties of flexible magnetic sheeting
| Code | Br | Hcb | Hcj | (BH)max | Forming way | Size | ||
| T | KA/m | KA/m | KJ/m3 | Max Length(m) | Max Width(mm) | Height(mm) | ||
| DXZY-1 | 0.13~0.18 | 80~120 | 100~160 | 4~6.4 | Calendering | 100 | 400 | 0.4~1.1 |
| DXZY-2 | 0.18~0.22 | 100~140 | 120~190 | 6.4~8.0 | Calendering | 2 | 930 | 0.6~3 |
| DXZY-3 | 0.21~0.239 | 140~165 | 150~210 | 8.0~10.4 | Calendering | 100 | 400 | 0.4~1.5 |
| DXZY-4 | 0.24~0.265 | 15z`6~181 | 200~270 | 10.4~12.5 | Calendering | 2 | 400 | 0.6~6 |
Physical properties of flexible magnetic sheeting
|
Code |
Tensile Strength (MPa) |
Elongation Rate (%) |
Hardness (SHA) |
Temperature (oC) |
Density (g/cm3) |
|
DXZY-1 |
7~12 |
100~200 |
85~98 |
-10~80 |
3.6~3.7 |
|
DXZY-2 |
7~12 |
100~300 |
85~98 |
-10~80 |
3.6~3.7 |
|
DXZY-3 |
7~12 |
100~200 |
85~98 |
-10~80 |
3.6~3.7 |
|
DXZY-4 |
7~12 |
100~300 |
85~98 |
-10~80 |
3.6~3.7 |